TYPE

Size

Description

Characterisic and Application

651-0615F

15-45

WC-Co

94/06

Agglomerated Sintered

。HVOF? APS

。fine WC

。Used for drawing equipment etc.

。Service temperature up to 500℃

。higher resistance to abrasion and corrosion resistance by low Co

。lower hardness ,strength and than WC88/12

。high bone strength

。Low Oxidation and corrosion resistance

651-1215

15-45

WC-Co88/12
Agglomerated Sintered

。HVOF? HVAF? APS

。median WC

。Service temperature up to 500℃

。Used for oil field apparetus, wire drawing equipment, fan and compressor blades,pump seals and housing, machine parts etc

。Hard and densen coating with high resistance to abrasion and erosion。Good bond strength

。High Oxidation and corrosion resistance

651-1215F

651-1210F

652-1215F

654-1245F

15-45

10-33

15-53

45-75

WC-Co88/12
Agglomerated Sintered

。HVOF? APS

。fine WC

。higher density

。（see651-1215）

651-1215N

651-1210N

652-1215N

654-1245N

15-45

10-33

15-53

45-75

WC-Co88/12
Agglomerated Sintered

。HVOF? APS

。nano size WC

。higher resistance to abrasion and corrosion resistance

。（see651-1215）

651-1715

?

?

15-45

WC-Co88/17
Agglomerated Sintered

。HVOF? HVAF? APS

。median WC

。Service temperature up to 500℃

。Used for turbine applications, extrusion dies,glass industry ,paper mill roll,pump parts,etc..

。Higher ductility due to higher Co content than WC-Co 88/12

。Hard and densen coating with high resistance to abrasion

。High sliding wear and erosion resistance

。Good bond strength

。High Oxidation and corrosion resistance

651-1715F

15-45

WC-Co88/17
Agglomerated Sintered

。HVOF

。fine WC

。higher resistance to abrasion

。（see651-1715）

653-0415

654-0445

?

?

?

15-45

45-75

WC-Co86/10/4
Agglomerated Sintered

。 HVAF HVOF? APS

。median WC

。Service temperature up to 500℃

。Used for paper rolls,gate and ball valves, hydraulic cylinders,compressor shafts ,etc

。Hard chrome replacement

。The CoCr matrix shows higher corrosion and abrasion resistance than the Co matrix

。Useable in water based solutions and wet corrosive environments

。Smooth coatings with fone microstructure and high bond strengths

651-0410F

651-0415F

654-0445F

10-33

15-45

45-75

WC-Co86/10/4
Agglomerated Sintered

。HVOF?? HVAF?? APS

。fine WC

。Higher corrosion resistance

。（see653-0415）

651-0410N

651-0415N

654-0445N

10-33

15-45

45-75

WC-Co86/10/4
Agglomerated Sintered

。HVOF?? HVAF?? APS

。nano size WC

。higher density bone strength

。（see 653-0415）

671-1015F

671-1020F

?

15-53

20-53

WC-Ni90/10

Agglomerated Sintered

。HVOF

。fine WC

。Service temperature up to 500℃

。Higher corrosion resistance than WC/Co

671-1515F

671-1520F

?

15-53

20-53

WC-Ni85/15

Agglomerated Sintered

。HVOF

。（see 671-1015）

。Higher ductility

671-1715F

671-1720F

?

15-53

20-53

WC-Ni83/17

Agglomerated Sintered

。HVOF

。（see671-1015），Higher ductility

681-2715F

?

15-45

WC-Cr3C2-Ni73/20/7
Agglomerated Sintered

。HVOF? HVAF

。fine WC

。Service temperature up to 750℃

。Used for gate valves .etc

。Higher oxidation and corrosion resistance

。Smooth coatings with fone microstructure and high bond strengths

871-2510

871-2522

871-2515

?

?

10-38

22-45

15-45

Cr3C2-NiCr75/25
Agglomerated Sintered

。HVOF

。median WC

。Service temperature up to 870℃

。Used for valve handle,turbine applications and fuel rod etc

。High erosion and corrosion resistance with dense coating

。High resistance to activation ,sliding wear and hot gas corrosion

871-2005

5-45

Cr3C2-NiCr80/20
Agglomerated Sintered

。HVOF

。Service temperature up to 870℃

。（see 791-2510）

。hardness ≥75/25